Method for producing trisphenols and monoester-substituted products  thereof, and 4-acylaralkylphenol derivatives

ABSTRACT

Trisphenols of general formula (1), which are useful as starting materials for polymer, are industrially easily produced by a method using as a starting material 4-aralkylphenol derivatives expressed by general formula (2): 
     
       
         
         
             
             
         
       
     
     wherein X represents a hydrogen atom or leaving group that can be substituted with a hydrogen atom.

TECHNICAL FIELD

The present invention relates to a method for producing with ease athigh yield and high purity in industrial settings trisphenols, which areuseful as materials for polymer compounds such as epoxy resins,polycarbonate resins or the like or as materials or additives forphotoresists. It also relates to a new 4-acylaralkylphenol derivativehaving a bisphenyl molecular skeleton with the acyl group in one phenylring and the hydroxyl group or acyloxy group in the other phenyl ring.Such compound is useful as various reactive materials having the effectof improving heat resistance, etc., especially as intermediate materialsfor generating trisphenols used as materials for polymer compounds suchas polycarbonate resins or the like or as materials for photoresists,etc., through reaction with phenols.

Among trisphenols, especially trisphenols other than of the trisphenolmethane type,1-[1,1-bis(4-hydroxyphenyl)ethyl]-4-[1-methyl-1-(4-hydroxyphenyl)ethyl]benzeneis known. These trisphenols are favorably used as materials for polymercompounds such as epoxy resins, polycarbonate resins or the like or asmaterials or additives for photoresists, etc. These trisphenols areknown to be obtained by reacting isopropenylacetophenone and phenols(Patent Literature 1).

However, this known material isopropenylacetophenone presents a problemin that it contains active olefin groups and thus has poor storagestability, and easily forms a polymer by readily undergoingpolymerization due to heat or impurities such as acid or the like aremixed in. Other problems of isopropenylacetophenone include high costand low yield of synthesis.

Accordingly, there is a need for a method for producing trisphenols withease and at high efficiency in industrial settings without using alkenylacetophenones such as isopropenylacetophenone or the like as thematerials, but using an readily available material offering high storagestability, as well as a need for a material compound that can be reactedwith phenols to produce trisphenols.

PRIOR ART LITERATURE Patent Literature

-   Patent Literature 1: Japanese Patent Laid-open No. Sho 62-084035

SUMMARY OF THE INVENTION Problems to Be Solved by the Invention

The present invention was developed to solve the aforementioned problemsassociated with the producing of trisphenols, and it is an object of thepresent invention to provide a method for producing trisphenols at highyield and high purity through reaction conditions that can beimplemented easily in industrial settings, without usingalkenylacetophenones as the starting materials, but using a materialthat offers excellent storage stability and can be obtained easily inindustrial settings. It is a further object of the present invention toprovide a method for producing monoester-substituted trisphenols, whichare useful as intermediate materials of trisphenols, reactive monomer,etc., that can be easily converted into trisphenols by eliminating theleaving group, and to provide a compound that can be reacted withphenols to generate trisphenols or compound that itself can be utilizedas various reactive compounds.

Means for Solving the Problems

After studying in earnest for ways to achieve the aforementionedobjects, the inventors completed the present invention by finding waysto achieve the aforementioned objects, as follows: For example, use, asthe starting material, 4-aralkylphenol derivatives according to generalformula (2) below that can be easily obtained by a known method using areadily available material, such as reacting phenols with styrenes or1-hydroxyalkylbenzenes, etc., and selectively nucleus-acylate thepara-position of the phenyl nucleus of the aralkyl group constitutingthe 4-aralkylphenols to obtain 4-acylaralkylphenol derivatives, afterwhich the leaving group of the obtained 4-acylaralkylphenol derivativesis substituted with a hydrogen atom to obtain 4-acylaralkylphenols, andthen cause the 4-acylaralkylphenols to undergo condensation reactionwith phenols in the presence of an acid catalyst, or cause the4-acylaralkylphenol derivatives to undergo condensation reaction withphenols in the presence of an acid catalyst, followed by substitutingthe leaving group of the obtained trisphenol derivatives with a hydrogenatom, to obtain the target trisphenols.

In addition, the inventors found a 4-acylaralkylphenol derivative havinga bisphenyl molecular skeleton with the acyl group at the para-positionin one phenyl ring and the hydroxyl group or acyloxy group at thepara-position in the other phenyl ring. By realizing that such compoundwas new and would easily generate a trisphenol when reacted with aphenol, or reacted with a phenol and the resulting acyloxy group washydrolyzed, and that this compound itself had two highly reactivefunction groups at both ends of the bisphenyl skeletal molecule so itcan be used as various reaction intermediates, the inventors completedthe present invention.

In other words, the present invention provides a method for producingtrisphenols expressed by general formula (1)

(in the formula, R₁ to R₄ each independently represent a hydrogen atom,alkyl group, alkoxyl group, aromatic hydrocarbon group, halogen atom,acyloxy group or hydroxyl group; R₅ and R₆ each independently representa hydrogen atom or alkyl group; R₇ represents a hydrogen atom or alkylgroup; R₀ represents an alkyl group, alkoxyl group or halogen atom; n is0 or an integer of 1 to 4, where if n is 2 or greater, all R₀'s may bethe same or different; and R₉ to R₁₁ each independently represent ahydrogen atom, alkyl group, alkoxyl group, aromatic hydrocarbon group,halogen atom or hydroxyl group),

wherein the producing method is characterized by using as the startingmaterial 4-aralkylphenol derivatives expressed by general formula (2)

(in the formula, R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (1), while X represents ahydrogen atom or leaving group that can be substituted with a hydrogenatom, where if n is 1 or greater, R₀ is not substituted at the4-position of the phenyl group).

Also, a method for producing trisphenols according to claim 1, wherein Xin general formula (2) is a leaving group that can be substituted with ahydrogen atom and this leaving group (hereinafter sometimes referred toas “Xa”) is an acyl group, is a favorable embodiment of the presentinvention.

In addition, a method for producing trisphenols according to claim 1,characterized by comprising a nucleus-acylation process (A) as well assubsequent phenols condensation process (B) and elimination process (C)for substituting Xa with a hydrogen atom, is a favorable embodiment ofthe present invention.

Process (A): Nucleus-acylate the 4-aralkylphenol derivatives expressedby general formula (2) above to obtain 4-acylaralkylphenol derivativesexpressed by general formula (3)

(in the formula, R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (2), while R₇ is the same as thecorresponding item in general formula (1) and Xa represents a leavinggroup that can be substituted with a hydrogen atom).

Process (B): Cause phenols expressed by general formula (4)

(in the formula, R₉ to R₁₁ are the same as the corresponding items ingeneral formula (1))

to undergo condensation reaction with the 4-acylaralkylphenolderivatives expressed by general formula (3) above as obtained byprocess (A), to obtain trisphenol derivatives expressed by generalformula (5)

(in the formula, R₁ to R₄, R₅ and R₆, R₀ and n, R₇, and R₉ to R₁₁ arethe same as the corresponding items in general formula (1), while Xarepresents a leaving group that can be substituted with a hydrogen atom)or, cause the aforementioned phenols to undergo condensation reactionwith the 4-acylaralkylphenols expressed by general formula (6) asobtained by process (C), to obtain trisphenols expressed by generalformula (1).

Process (C): Eliminate the Xa group of the 4-acylaralkylphenolderivatives expressed by general formula (3) as obtained by process (A),to obtain 4-acylaralkylphenols expressed by general formula (6)

(in the formula, R₁ to R₄, R₅ and R₆, R₀ and n, and R₇ are the same asthe corresponding items in general formula (1)) or, eliminate the Xagroup of the trisphenol derivatives expressed by general formula (5) asobtained by process (B), to obtain trisphenols expressed by generalformula (1).

A method for producing trisphenols according to claim 1, wherein generalformula (2) above is expressed as general formula (2a) where X is anacyl group, or as general formula (2b) where X is a hydrogen atom, andsaid producing method comprises processes A1, C1 and B1 in this sequence(first producing method) or processes A1, B2 and C2 in this sequence(second producing method), is a favorable embodiment of the presentinvention.

Process A1: Nucleus-acylate 4-aralkylphenylesters expressed by generalformula (2a)

(in the formula, R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (2), while R₈ represents ahydrogen atom or hydrocarbon group, where if n is 1 or greater, R₀ isnot substituted at the 4-position of the phenyl group)or, 4-aralkylphenols expressed by general formula (2b)

(in the formula, R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (2), where if n is 1 or greater,R₀ is not substituted at the 4-position of the phenyl group)to obtain 4-acylaralkylphenylesters expressed by general formula (7)

(in the formula, R₁ to R₄, R₅ and R₆, R₀, and n and R₇ are the same asthe corresponding items in general formula (1), while R₈ is the same asthe corresponding item in general formula (2a)).

Process C1: Hydrolyze, alcoholyze or phenolyze the ester group of the4-acylaralkylphenylesters expressed by general formula (7), to obtain4-acylaralkylphenols expressed by general formula (6) above.

Process B1: Next, cause the obtained 4-acylaralkylphenols to undergocondensation reaction with phenols expressed by general formula (4)above, to obtain trisphenols expressed by general formula (1).

Process B2: Cause 4-acylaralkylphenylesters expressed by general formula(7) to undergo condensation reaction with phenols expressed by generalformula (4), to obtain monoester-substituted trisphenols expressed bygeneral formula (8)

(in the formula, R₁ to R₄, R₅ and R₆, R₀ and n, R₇, and R₉ to R₁₁ arethe same as the corresponding items in general formula (1), while R₈ isthe same as the corresponding item in general formula (2a)).

Process C2: Next, hydrolyze, alcoholyze or phenolyze the ester group ofthe obtained monoester-substituted trisphenols, to obtain trisphenolsexpressed by general formula (1).

The present invention also provides 4-acylaralkylphenols expressed byformula (6) above, as well as 4-acylaralkylphenylesters expressed byformula (7) above which is a derivative of 4-acylaralkylphenol.

Effects of the Invention

According to the method for producing trisphenols proposed by thepresent invention, 4-aralkylphenol or derivative thereof used as thestarting material is relatively stable against acid and heat and offersexcellent storage stability, which is a plus in industrial production,and it can be produced with ease from inexpensive, readily availablestarting materials such as phenols, styrenes or the like. After this4-aralkylphenol or derivative thereof is nucleus-acylated, it is causedto undergo condensation reaction with phenols and the leaving group ofthe 4-acylaralkylphenol derivatives is substituted with a hydrogen atom,to obtain trisphenols of various structures suitable for variouspurposes. It is also possible to obtain each target product at highpurity and high yield by selecting a specified leaving group or reactionmethod.

In addition, the 4-acylaralkylphenol derivative proposed by the presentinvention is a new 4-acylaralkylphenol derivative having a bisphenylmolecular skeleton with the acyl group at the para-position in onephenyl ring and the hydroxyl group or acyloxy group at the para-positionin the other phenyl ring, and when it is reacted with phenols,trisphenols of various structures suitable for various purposes can beobtained at high purity and high yield. Since this 4-acylaralkylphenolderivative itself has two highly reactive function groups at both endsof the bisphenyl skeletal molecule, it can be used as intermediatereaction products of various types offering excellent heat resistance,etc.

Furthermore, such compound is more stable against acid and heat andoffers excellent storage stability compared to conventional materialcompounds, and can be produced from 4-aralkylphenols which can yet beeasily produced from an inexpensive, readily available materials such asphenols or styrenes or the like.

BEST MODE FOR CARRYING OUT THE INVENTION

Under the present invention, the target trisphenols expressed by generalformula (1) are produced from the starting material being4-aralkylphenol derivatives expressed by general formula (2), through anucleus-acylation process (A) as well as subsequent phenols condensationprocess (B) and elimination process (C) for substituting X with ahydrogen atom.

A scheme of a producing method conforming to the present invention isshown below.

As for the 4-aralkylphenol derivatives expressed by general formula (2),which are used as the materials in the method for producing trisphenolsproposed by the present invention, in the formula R₁ to R₄ eachindependently represent a hydrogen atom, alkyl group, alkoxyl group,aromatic hydrocarbon group, halogen atom, acyloxy group or hydroxylgroup; R₅ and R₆ each independently represent a hydrogen atom or alkylgroup; R₀ represents an alkyl group, alkoxyl group or halogen atom; n is0 or an integer of 1 to 4, where if n is 2 or greater, all R₀'s may bethe same or different.

Here, if R₁ to R₄ are an alkyl group, it may be a straight or branchedalkyl group with 1 to 10 carbon atoms, or cycloalkyl group with 5 to 10carbon atoms. Preferably it is a straight or branched alkyl group with 1to 4 carbon atoms, or cycloalkyl group with 5 or 6 carbon atoms.Specific examples of such alkyl group include the methyl group, ethylgroup, n-propyl group, isopropyl group and cyclohexyl group, etc.

The alkyl group may also have a substituent such as a halogen atom,alkoxyl group, hydroxyl group, acyloxy group, phenyl group or the like.Accordingly, specific examples of the alkyl group include the methylgroup, ethyl group, isopropyl group, cyclohexyl group, benzyl group,methoxy ethyl group and 3-chloropropyl group, etc.

Also, the alkoxyl group may be, for example, a straight or branchedalkoxyl group with 1 to 10 carbon atoms, or cycloalkoxyl group with 5 to10 carbon atoms. Preferably it is a straight or branched alkoxyl groupwith 1 to 4 carbon atoms, where if an alkoxyl group with 3 or 4 carbonatoms is used, it may be of straight or branched type. A preferred formof the cycloalkoxyl group is a cycloalkoxyl group with 5 or 6 carbonatoms. Specific examples of such alkoxyl group include the methoxygroup, ethoxy group, n-propoxy group, isopropoxy group and cyclohexyloxygroup, etc. R₁ to R₄ are preferably a hydrogen atom, alkyl group with 1to 8 carbon atoms, or alkoxyl group with 1 to 8 carbon atoms, or morepreferably are a hydrogen atom or alkyl group with 1 to 4 carbon atoms.In addition, R₃ or R₄ preferably are a hydrogen atom, methyl group orethyl group, and more preferably either R₃ or R₄ or both is/are hydrogenatom.

The alkyl group of the alkoxyl group may also have a substituent such asa halogen atom, alkoxyl group, hydroxyl group, acyloxy group, phenylgroup or the like. Accordingly, specific examples of the alkoxyl groupinclude the methoxy group, ethoxy group and 2-chloroethoxy group, etc.

If an aromatic hydrocarbon group is used, it may be an aromatichydrocarbon group with 6 to 10 carbon atoms, for example. The aromatichydrocarbon group may also have a substituent such as an alkyl group,halogen atom, alkoxyl group, hydroxyl group, acyloxy group, phenyl groupor the like. Accordingly, specific examples of the aromatic hydrocarbongroup include the phenyl group, 1-naphtyl group, 4-methylphenyl groupand 4-chlorophenyl group, etc. If the aromatic hydrocarbon group is aphenyl group, preferably the 4-position of the phenyl group has asubstituent.

Examples of the halogen atom include bromine, chlorine, fluorine andiodine.

As for the acyloxy group (R—C(O)—O—), the substituent (R) bonded to itscarbonyl group may be an aliphatic hydrocarbon group, cyclic hydrocarbongroup, aromatic hydrocarbon group or hydrogen atom, but it is preferablyan alkyl group or aromatic hydrocarbon group similar to the alkyl groupor aromatic hydrocarbon group used when R₁ to R₄ mentioned above are analkyl group or aromatic hydrocarbon group, or more preferably is analkyl group similar to the aforementioned alkyl group.

Accordingly, specific examples of the acyloxy group include theformyloxy group, acetyloxy group, propionyloxy group, benzoyloxy groupand toluoyloxy group, etc.

If at least one of R₁ to R₄ is a hydroxyl group or acyloxy group,preferably both R₁ and R₂ are not a hydroxyl group or acyloxy groupsimultaneously, and both R₁ and R₃ are a hydroxyl group or acyloxy groupor either R₁ or R₃ is a hydroxyl group or acyloxy group, or morepreferably either R₃ or R₄ or both is/are hydrogen atom.

As for the 4-aralkylphenol derivatives expressed by general formula (2)above, in the formula R₅ and R₆ each independently represent a hydrogenatom or alkyl group, where if an alkyl group is used, it may be astraight or branched alkyl group with 1 to 10 carbon atoms, orcycloalkyl group with 5 to 10 carbon atoms, for example. Preferably itis a straight or branched alkyl group with 1 to 10 carbon atoms, or morepreferably an alkyl group with 1 to 4 carbon atoms, where if an alkylgroup with 3 or 4 carbon atoms is used, it may be of straight orbranched type. Specific examples include the methyl group, ethyl group,n-propyl group, isopropyl group and sec-butyl group etc. Note that whileeither R₅ or R₆ may be a hydrogen atom or both may be an alkyl group orhydrogen atom, preferably either R₅ or R₆ or both is/are a hydrogen atomor primary or secondary alkyl group.

R₀ represents an alkyl group, alkoxyl group or halogen atom, where thisalkyl group, alkoxyl group or halogen atom is the same as the alkylgroup, alkoxyl group or halogen atom used when R₁ to R₄ mentioned aboveare an alkyl group, alkoxyl group or halogen atom. The alkyl group isstraight or branched, where specific examples of such alkyl groupinclude the methyl group, ethyl group, n-propyl group, isopropyl groupand sec-butyl group, etc. If an alkoxyl group is used, it is straight orbranched, where specific examples of such alkoxyl group include themethoxy group, ethoxy group, n-propoxy group, isopropoxy group andsec-butoxy group etc.

n is 0 or an integer of 1 to 4, but if n is 2 or greater, all R₀'s maybe the same or different. Preferably n is 0 or an integer of 1 or 2. R₀preferably is an alkyl group with 1 to 4 carbon atoms.

X represents a hydrogen atom or leaving group that can be substitutedwith a hydrogen atom (hereinafter also referred to as “Xa”). Here, theleaving group that can be substituted with a hydrogen atom is preferablysuch that after 4-aralkylphenol derivatives expressed by general formula(2) have been put through the nucleus-acylation process (A), the leavinggroup (Xa) bonded with the 4-acylaralkylphenol derivatives expressed bygeneral formula (3) or trisphenol derivatives expressed by generalformula (5) can be substituted with a hydrogen atom without affectingthe 4-acyl group, aralkyl phenol skeleton or trisphenol skeleton. Forexample, it may be a substituent that can be easily eliminated throughhydrolysis, alcoholysis, hydrogenolysis, cleavage reaction, etc., whereexamples of such leaving group (Xa) include the acyl group, hydrocarbongroup and residue obtained by removing the hydroxyl group from sulfonicacid (R′—SO₂ group; R′ represents a hydrocarbon group), etc. To bespecific, it may be groups such as the alkylcarbonyl group, alkyl group,alkylsulfonyl group, arylsulfonyl group or the like. Specific examplesinclude the acetyl group, 4-methylphenylcarbonyl group, methyl group,cyclohexyl group, mesyl group, trifluoromethylsulfonyl group, tosylgroup and 2-nitrobenzenesulfonyl group, where the acyl group ispreferred, and the alkylcarbonyl group such as the acetyl group or thelike is more preferred, because it suppresses decomposition of thealkylidene group in the material 4-aralkylphenol derivative expressed bygeneral formula (2) and improves the selectivity of nucleus-acylationreaction.

Accordingly, specific examples of the 4-aralkylphenol derivativesexpressed by general formula (2) include p-cumylphenol,2-methyl-4-cumylphenol, 2,6-dimethyl-4-cumylphenol,2,3,6-trimethyl-4-cumylphenol, 4-benzylphenol, 4-(1-phenylethyl)phenol,2-chloro-4-cumylphenol,2-chloro-4-[(2,5-dimethylphenyl)methyl]-6-methylphenol,2-phenyl-4-benzylphenol, 1-(4-acetoxyphenyl)-1-methylethylbenzene,1-tosyloxy-4-(1-phenyl-1-methylethyl)benzene,1-mesyloxy-4-(1-phenyl-1-methylethyl)benzene and1-methoxy-4-(1-phenyl-1-methylethyl)benzene, etc.

Such 4-aralkylphenols can be easily obtained through reaction of phenolsand styrenes or 1-hydroxy alkylbenzenes according to the methodsdescribed in U.S. Pat. No. 2,247,402, U.S. Pat. No. 2,714,120 and U.S.Pat. No. 2,769,844, etc.

If X is an acyl group, such 4-aralkylphenylesters can be easily obtainedby any known method of acylation, such as one where the phenolichydroxyl group of the 4-aralkylphenol is acylated using acylation agentsuch as acetic anhydride, propionyl chloride or the like.

If X is a hydrocarbon group, such hydrocarbon group may be similar toone used when R₁ to R₄ mentioned above are an aromatic hydrocarbon groupor alkyl group. If X is an alkyl group, it may be a straight, branchedor cyclic alkyl group with around 1 to 10 carbon atoms, where loweralkyl group such as the methyl group, ethyl group, propyl group or thelike is preferable. Such 4-aralkylphenyl ethers can be easily obtainedby any known method, such as one where a 4-aralkylphenol is reacted witha halogenated alkyl in the presence of a base (reaction formula: Example1). It can also be obtained by reacting alkoxylbenzenes and styrenes inthe presence of catalyst such as lithium iodine, bismuth trichloride orthe like (reaction formula: Example 2) as described in TetrahedoronLetters 48 (2007) 6881-6885 and Euro. J. Org. Chem. 2006, 4231-4236.

Reaction Formula Example 1

Reaction Formula Example 2

If X is a residue obtained by removing the hydroxyl group from sulfonicacid (R′—SO₂ group; R′ represents a hydrocarbon group), in generalformula (2), the hydrocarbon group R′ is similar to one used when R₁ toR₄ mentioned above are an aromatic hydrocarbon group or alkyl group, andsuch 4-aralkylphenol derivative whose X is a residue obtained byremoving the hydroxyl group from sulfonic acid can be easily obtained byany known method such as one where 4-aralkylphenols expressed by generalformula (2b) are reacted with halogenated sulfonyl hydrocarbon such astosyl chloride, mesyl chloride or the like in the presence of organicamine such as pyridine or the like or inorganic base such as potassiumcarbonate or the like.

In the meantime, with respect to the target product of the presentinvention, or specifically trisphenols expressed by general formula (1)above, in the formula R₁ to R₄, R₅ and R₆, R₀ and n are the same as thecorresponding items in general formula (2).

R₇ represents a hydrogen atom or alkyl group, where if an alkyl group isused, it is the same as the alkyl group used when R₁ to R₄ mentionedabove are an alkyl group, and it is preferably of primary or secondarytype. Accordingly, specific examples of such alkyl group include themethyl group, ethyl group, isopropyl group, cyclohexyl group, benzylgroup, methoxyethyl group and 3-chloropropyl group, etc. Also, the alkylgroup preferably has 1 to 4 carbon atoms.

Also, R₉ to R₁₁ each independently represent a hydrogen atom, alkylgroup, alkoxyl group, aromatic hydrocarbon group, halogen atom orhydroxyl group, where the alkyl group, alkoxyl group, aromatichydrocarbon group or halogen atom is the same as the alkyl group,alkoxyl group, aromatic hydrocarbon group or halogen atom used when R₁to R₄ mentioned above are an alkyl group, alkoxyl group, aromatichydrocarbon group or halogen atom, and a hydrogen atom, alkyl group with1 to 4 carbon atoms, cycloalkyl group with 5 or 6 carbon atoms, alkoxylgroup with 1 to 4 carbon atoms, or phenyl group is preferred. It is alsopreferable from the production viewpoint that both R₉ and R₁₀ should notbe a hydroxyl group simultaneously, and if R₇ is an alkyl group,preferably R₁₁ is a hydrogen atom from the production viewpoint.

Accordingly, specific examples of the trisphenols expressed by generalformula (1) include the following, and the like:

-   1-[α-methyl-α-(3-methyl-4-hydroxyphenyl)ethyl]-4-[α,α-bis(3-methyl-4-hydroxyphenyl)ethyl]benzene;-   1-[α-methyl-α-(3-methoxy-4-hydroxyphenyl)ethyl]-4-[α,α-bis(3-methoxy-4-hydroxyphenyl)ethyl]benzene;-   1-[α-methyl-α-(4-hydroxyphenyl)ethyl]-4-[α,α-bis(4-hydroxyphenyl)ethyl]    benzene; and-   1-[α-methyl-α-(3-cyclohexyl-4-hydroxyphenyl)ethyl]-4-[α,α-bis(3-cyclohexyl-4-hydroxyphenyl)ethyl]benzene.

Also regarding the 4-aralkylphenylesters expressed by general formula(2a), which are one of the 4-aralkylphenol derivatives expressed bygeneral formula (2) and used as the material in the method for producingtrisphenols proposed by the present invention, in the formula R₁ to R₄,R₅ and R₆, R₀ and n are the same as the corresponding items in generalformula (2). R₈ is a hydrogen atom or hydrocarbon group, and if ahydrocarbon group is used, it may be an unsaturated aliphatichydrocarbon group, alkyl group or aromatic hydrocarbon group, etc. If analkyl group or aromatic hydrocarbon group is used, it is the same as thealkyl group or aromatic hydrocarbon group used when R₁ to R₄ are analkyl group or aromatic hydrocarbon group in general formula (2). Analkyl group is preferable, and as the species, an alkyl group of primaryor secondary type is preferable.

As for the 4-aralkylphenyl ethers expressed by general formula (2c),which are a one of 4-aralkylphenol derivatives expressed by generalformula (2) and used as the material in the method for producingtrisphenols proposed by the present invention, in the formula R₁ to R₄,R₅ and R₆, R₀ and n are the same as the corresponding items in generalformula (2), where R represents a hydrocarbon group. The hydrocarbongroup constituting R may be an unsaturated aliphatic hydrocarbon group,alkyl group or aromatic hydrocarbon group, etc. If an alkyl group oraromatic hydrocarbon group is used, it is the same as the alkyl group oraromatic hydrocarbon group used when R₁ to R₄ are an alkyl group oraromatic hydrocarbon group in general formula (2). An alkyl group ispreferable, and as the species, an alkyl group of primary or secondarytype is preferable.

Under the method for producing trisphenols proposed by the presentinvention, it is preferable to use reaction scheme 1 as shown below forproduction if X in the 4-aralkylphenol derivative being the materialexpressed by general formula (2) is an acyl group according to generalformula (2a) or is a hydrogen atom according to general formula (2b):

Next, processes A1 and A under the producing method proposed by thepresent invention are explained.

Under the producing method proposed by the present invention,4-aralkylphenol derivatives expressed by general formula (2) above, orpreferably 4-aralkylphenylesters expressed by general formula (2a) or4-aralkylphenols expressed by general formula (2b) above, are used asthe starting materials. Then, as illustrated by the producing scheme,the starting materials are nucleus-acylated in process A1 usingacylation agent such as acetylchloride, acetic anhydride or the like ifthe starting materials are 4-aralkylphenylesters expressed by generalformula (2a), after which an acyl group is introduced to the 4-positionof the phenyl group in the aralkyl group to obtain4-acylaralkylphenylesters expressed by general formula (7). The startingmaterials, or 4-aralkylphenylesters expressed by general formula (2a),can be obtained by, for example, acylating the hydroxyl group of4-aralkylphenols expressed by general formula (2b) that corresponds togeneral formula (2) where X is a hydrogen atom.

If the starting materials are 4-aralkylphenols expressed by generalformula (2b), 4-acylaralkylphenylesters expressed by general formula (7)can also be obtained via acylation of the hydroxy group andnucleus-acylation of the phenyl group using the same reaction process inprocess A1. In this case, the hydroxyl group is acylated first, and thenthe phenyl group is nucleus-acylated. Also when the starting materialsare 4-aralkylphenol derivatives expressed by general formula (2) where Xis a leaving group other than the acyl group, 4-acylaralkylphenolderivatives expressed by general formula (3), whose leaving group Xacorresponds to that of the material 4-aralkylphenol derivatives, can beobtained via nucleus-acylation in the same manner as when the4-aralkylphenylester expressed by general formula (2a) is used.

Any known acylation reaction can be used for the nucleus-acylationreaction, or acylation reaction of the hydroxy group. Any acylationagent can be used as long as it is being used as such, but it preferablyis halogenated acyl expressed by general formula (11) below orcarboxylic acid anhydride expressed by general formula (12) below, etc.:

(in the formula, R₇ represents a hydrogen atom or alkyl group, R₈represents a hydrogen atom or hydrocarbon group, Y represents a halogenatom, and R₇ or R₈ corresponds to R₇ or R₈ in general formula (7),respectively).

The alkyl group constituting R₇ is the same as the alkyl group used whenR₁ to R₄ are an alkyl group in general formula (2), while thehydrocarbon group constituting R₈ may be an unsaturated aliphatichydrocarbon group, alkyl group or aromatic hydrocarbon group, etc.,where the alkyl group or aromatic hydrocarbon group is the same as thealkyl group or aromatic hydrocarbon group used when R₁ to R₄ are analkyl group or aromatic hydrocarbon group in general formula (2).

Accordingly, specific examples of the acylation agent suitable forgeneral formula (11) or general formula (12) having the substituent R₇include formylchloride, acetylchloride, acetylbromide, propionylchloride, acetic anhydride, monochloroacetic acid anhydride andpropionic anhydride, etc., while specific examples of the acylationagent suitable for general formula (11) or general formula (12) havingthe substituent R₈ include formylchloride, acetylchloride,acetylbromide, propionyl chloride, benzoyl chloride, toluic acidchloride, acetic anhydride, monochloroacetic acid anhydride, propionicanhydride, succinic anhydride and maleic anhydride, etc.

Acylation in process A1 of the 4-aralkylphenols expressed by generalformula (2b) above may be such that the hydroxyl group and phenyl ringof the 4-aralkylphenol are acylated simultaneously (process A1b below:one-stage method), or the hydroxyl group is protected with acyl groupsuch as an acetyl group or the like first, followed by nucleus-acylationof the phenyl ring (process A1a below: two-stage method). The formerone-stage acylation method is preferable. The nucleus-acylation reactionin process A1a below is the same as nucleus-acylation reaction inprocess A1 when the starting material above is 4-aralkylphenylestersexpressed by general formula (2a).

[Process A1b: Reaction Scheme for One-Stage Acylation]

Under this method, the hydroxyl group and phenyl nucleus are acylated inone stage, which means R₇═R₈ and for the acylation agent, one suitablefor general formula (11) or general formula (12) having the substituentR₇ is used, for example.

[Process A1a: Reaction Scheme for Two-Stage Acylation]

Under this method, acylation is implemented in two stages, which meansR₇ and R₈ may be the same or different and for the acylation agent, onesuitable for general formula (11) having the substituent R₈, generalformula (11) having acylation agent suitable for general formula (12)and the substituent R₇, and general formula (12) are used in sequence.

Accordingly, in the 4-acylaralkylphenol derivative expressed by generalformula (3) and in R₇ in the formula and 4-acylaralkylphenylestersexpressed by general formula (7), the substituent R₇ or R₈ in theformula is derived from R₇ or R₈ being a halogenated acyl which is theacylation agent used in the acylation process expressed by generalformula (11) above, or carboxylic acid anhydride expressed by generalformula (12) above. Under the one-stage acylation method where thehydroxyl group and phenyl group are acylated at the same time in processA1, R₇ and R₈ are the same. Under the two-stage acylation process wherethe hydroxyl group is acylated first and then the phenyl nucleus isacylated, R₇ and R₈ may be the same or different.

Normally an acylation catalyst is used in acylation reaction. Anyacylation catalyst can be used as long as it is an acid catalyst capableof acylating carbon atoms in aromatic rings such as the benzene ring orthe like, but examples include Lewis acid, solid acid and protonic acid,etc.

Examples of Lewis acid include metal halogenides such as aluminumchloride, tin chloride (IV), copper chloride, (anhydrous) ferricchloride (III) or the like, but aluminum chloride is preferred. Examplesof solid acid include heteropolyacids such as zeolite, phosphotungsticacid, phosphomolybdic acid, silicotungstic acid, silicomolybdic acid orthe like, and metal salts of heteropolyacids, etc. Examples of protonicacid include hydrogen chloride gas, sulfuric acid and polyphosphoricacid, etc. Of the above, Lewis acid is preferred.

The molar ratio of acylation agent to 4-aralkylphenol derivativesexpressed by general formula (2) (acylation agent/4-aralkylphenolderivatives) preferably is in a range of [{1+(number of hydroxyl groupsin 4-aralkylphenol derivatives molecule)}]/1 to [1.25×{1+(number ofhydroxyl groups in 4-aralkylphenol derivatives molecule)}]/1. Forexample, in the case of 4-aralkylphenols expressed by general formula(2b) where X is a hydrogen atom and there is no other hydroxyl group,the diacylation method where the hydroxyl group and phenyl nucleus areacylated in the same reaction process (one-stage acylation method)preferably uses a range of 2/1 to 2.5/1, or more preferably a range of2.1/1 to 2.3/1. On the other hand when acylating only the phenyl nucleusof 4-aralkylphenol derivatives where X is not a hydrogen atom and thereis no hydroxyl group, the range preferably is 1/1 to 1.25/1, or morepreferably is 1.1/1 to 1.2/1. The aforementioned hydroxyl grouppreferably is a phenolic hydroxyl group.

If Lewis acid is used, the molar ratio of Lewis acid to carbonyl groupsin acylation agent (number of moles in Lewis acid/[number of moles inacylation agent x number of carbonyl groups in acylation agentmolecule]) preferably is in a range of 1/1 to 1/1.1, or more preferablyis 1/1. If the molar ratio is too high, the yield drops. Too low a molarratio is not desirable, either, because the reaction ratio of acylationagent drops.

Specifically, the molar ratio of Lewis acid to acylation agent (Lewisacid/acylation agent) preferably is in a range of 1/1 to 1/1.1, or morepreferably is 1/1, in the case of halogenated acyl. If an acid anhydrideis used, the molar ratio preferably is in a range of 2/1 to 2/1.1, ormore preferably is 2/1. If the 4-aralkylphenol derivatives expressed bygeneral formula (2) have oxo (═O) such as an acyloxy group, alkylsulfonyloxy group or the like then the molar volume of Lewis acid usedpreferably is in a range of (number of moles in acylation agent x numberof carbonyl groups in acylation agent molecule) to ([number of moles inacylation agent x number of carbonyl groups in acylation agentmolecule]+[number of moles in 4-aralkylphenol derivatives x number ofoxo groups in 4-aralkylphenol derivatives molecule]). Therefore, whenacylating 4-aralkylphenol derivatives where X is an acyloxy group andthere is no oxo group or hydroxyl group, for example, the molar ratio(Lewis acid/acylation agent) preferably is in a range of 1/1 to 2/1 ifthe acylation agent is a halogenated acyl. In the case of an acidanhydride, the molar ratio (Lewis acid/acylation agent) preferably is ina range of 1/1 to 3/1.

Depending on the activity of the catalyst used, an excessively highreaction temperature makes it easy to cause a side reaction, such as theR₅ and R₆ substituted alkylidene group being severed, etc., therebyresulting in low yield. Accordingly, the reaction temperature preferablyis in a range of −50 to 50° C., or −20 to 20° C. when Lewis acid isused, or more preferably is in a range of 0 to 10° C.

For this reaction, a reaction solvent generally used for Friedel-Craftsreaction is normally used. Solvents that can be used include halogenatedsaturated hydrocarbons such as chloroform, methylenechloride or thelike, as well as chlorobenzene and carbon disulfide.

Under these reaction conditions, the reaction normally completes inseveral hours up to less than ten plus several hours if Lewis acid isused, and the reaction process normally takes the form of mixing Lewisacid and acylation agent to form a complex (or adduct) and then drippinga solution of 4-aralkylphenol derivatives into a solution of thiscomplex.

If the acylation agent is formylhalogen, the compound itself is unstableand thus carbon monoxide and hydrogen chloride can also be used toimplement the above acylation reaction in the presence of aluminumchloride or copper chloride.

In the case of two-stage acylation where the hydroxyl group of the4-aralkylphenol is protected by acyl group such as an acetyl group orthe like and then the phenyl ring is nucleus-acylated, the hydroxylgroup is acylated first, after which the same acylation reaction isrepeated using the same acylation agent or a different acylation agent.In this case, use of an excessive amount of carboxylic acid anhydride inthe first reaction, or acylation of the hydroxyl group, is preferredbecause this normally eliminates the need for Lewis acid and makes thereaction easy.

Also, any known refining method can be used to refine the target productfrom the liquid reaction mixture, as necessary. If the catalyst is Lewisacid, for example, acid aqueous solution such as aqueous solution ofhydrochloric acid or the like is added to decompose the adduct of theacid and product to deactivate the acid and dissolve it in the waterlayer. If necessary, a solvent that separates from water is added toseparate and remove the water layer to obtain the oil layer. Theobtained oil layer is washed in water and the solvent and material(phenols, if multi-nuclear) are distilled out from the obtained oillayer as necessary, after which a solvent is added to causecrystallization or precipitation to obtain crystalline ornon-crystalline solids. If necessary, such as when the purity of crystalor solids is low, etc., recrystallization or reprecipitation may berepeated once or multiple times. This way, highly pure4-acylaralkylphenylesters can be achieved in process A1.

Specific examples of such 4-acylaralkylphenylesters include thefollowing or the like:

-   1-acetyl-4-{1-methyl-1-(4-acetyloxyphenyl)ethyl}benzene;

-   1-acetyl-4-{1-methyl-1-(3-methyl-4-acetyloxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(3,5-dimethyl-4-acetyloxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(2,3,5-trimethyl-4-acetyloxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(3-cyclohexyl-4-acetyloxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(3-isobutyl-4-acetyloxyphenyl)ethyl}benzene;-   1-butyryl-4-{1-methyl-1-(4-butyryloxyphenyl)ethyl}benzene;-   1-acetyl-4-{(4-acetyloxyphenyl)methyl}benzene;-   1-acetyl-4-{1-(4-acetyloxyphenyl)ethyl}benzene; and-   1-propionyl-4-{(4-acetyloxyphenyl)methyl}benzene.

Next, processes C1 and B1 in the producing method proposed by thepresent invention are explained.

Process C1 is a reaction process to obtain 4-acylaralkylphenolsexpressed by general formula (6) by hydrolyzing, alcoholyzing and/orphenolyzing the ester group of the 4-acylaralkylphenylesters expressedby general formula (7) as obtained in process A1 above, according to theaforementioned reaction scheme, while process B1 is a reaction processto obtain the target product, or trisphenols expressed by generalformula (1), by subsequently causing the obtained 4-acylaralkylphenolsto undergo condensation reaction with a phenol expressed by generalformula (4).

In process C1, any known method can be used for hydrolysis, alcoholysisor phenolysis of the ester group. In the case of decomposition usingwater, alcohols and/or phenols, for example, there is no limitationregarding the molar ratio of water, alcohols and/or phenols to4-acylaralkylphenylesters ([water, alcohols and/orphenols]/4-acylaralkylphenylesters), but it should normally be in arange of 1/1 to 100/1, or preferably is in a range of 10/1 to 30/1,because if the molar ratio is too high, the volume efficiency drops.Also for alcohol, aliphatic alcohol such as methanol, ethanol or thelike is preferred. For phenol, mononuclear phenol such as phenol,o-cresol or the like is preferred.

The decomposition reaction is normally implemented in the presence of analkali or acid catalyst, but use of alkali is preferred from theviewpoints of reaction speed and yield. Examples of alkali includealkali metal hydroxides such as sodium hydroxide, potassium hydroxide orthe like, as well as organic strong bases such as tetramethyl ammoniumhydroxide, or the like. The molar ratio of alkali to4-acylaralkylphenylesters (alkali/number of ester groups in4-acylaralkylphenylesters molecule) should normally be in a range of 1/1to 5/1, or preferably is in a range of 2/1 to 3/1.

The reaction temperature should normally be in a range of 0 to 150° C.,or preferably is in a range of 50 to 100° C. If the material4-acylaralkylphenylesters has a high melting point and agitation isdifficult at the time of reaction, a solvent can be used. Any solventcan be used as long as it does not inhibit the reaction or cause anyside reaction, but examples include aliphatic ketones such as methylisobutyl ketone or the like, lower aliphatic alcohols such as methanol,isopropanol or the like, aromatic hydrocarbons such as toluene or thelike, and ethers such as tetrahydrofuran or the like. If water alone isused to implement hydrolysis, preferably a small amount of water-solublealcohol such as methanol is added to water because otherwise thereaction speed is too slow.

After the reaction, any known refining method can be used to refine thetarget product from the liquid reaction mixture, as necessary. Forexample, an aqueous solution of acid is added to the obtained liquidreaction mixture to neutralize the alkali, and if necessary a solventthat separates from water is added to separate and remove the waterlayer and obtain the oil layer containing the target product. Theobtained oil layer is washed with water and, after distilling out thesolvent, etc., from the obtained oil layer as necessary, a solvent isadded again to cause crystallization or precipitation to obtaincrystalline or non-crystalline solids. If necessary, such as when thepurity of crystal or solids is low etc., recrystallization orreprecipitation may be repeated once or multiple times. This way, highlypure 4-acylaralkylphenols expressed by general formula (6) can beachieved.

Specific examples of such 4-acylaralkylphenols include following, or thelike:

-   1-acetyl-4-{1-methyl-1-(4-hydroxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(3-methyl-4-hydroxyphenyl)ethyl}benzene;

-   1-acetyl-4-{1-methyl-1-(3,5-dimethyl-4-hydroxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(2,3,5-trimethyl-4-hydroxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(3-cyclohexyl-4-hydroxyphenyl)ethyl}benzene;-   1-acetyl-4-{1-methyl-1-(3-isobutyl-4-hydroxyphenyl)ethyl}benzene;-   1-butyryl-4-{1-methyl-1-(4-hydroxyphenyl)ethyl}benzene;-   1-acetyl-4-{(4-hydroxyphenyl)methyl}benzene; and-   1-acetyl-4-{1-(4-hydroxyphenyl)ethyl}benzene.

Next in process B1, the 4-acylaralkylphenols obtained above are causedto undergo condensation reaction with phenols expressed by generalformula (4) to obtain trisphenols. Any known reaction method can be usedfor the condensation reaction. Here, specific examples of the phenolsexpressed by general formula (4) include phenol, o-cresol,2-ethylphenol, catechol, 2-cyclohexylphenol, 2-methoxyphenol,2-isopropylphenol, 2-chlorophenol, 2-bromophenol, 2-phenylphenol,2-benzylphenol and 2,6-xylenol, etc.

At the time of reaction, the molar ratio of phenols to4-acylaralkylphenols (phenols/4-acylaralkylphenols) should normally bein a range of 2/1 to 10/1, or preferably is in a range of 3/1 to 5/1.The catalyst used for the reaction preferably is an inorganic acid ororganic acid of high to medium strength. Examples of inorganic acidinclude 35% hydrochloric acid, hydrogen chloride gas, sulfuric acid andphosphoric acid, etc. Preferred forms of organic acid are organicsulfonic acid and carboxylic acid, where examples include p-toluenesulfonic acid, methane sulfonic acid and oxalic acid, etc. Of these, astrong acid, especially hydrochloric acid gas or concentratedhydrochloric acid is preferred. The amount of catalyst used variesdepending on the type of catalyst, but normally it should be in range of1 to 50 percent by weight relative to phenols. Also, use of anappropriate amount of co-catalyst with the main catalyst is preferablebecause it improves the yield, especially when R₇ in general formula (6)is an alkyl group.

For the co-catalyst, a compound or polymer compound containing amercapto group is preferred, where specific examples include alkylmercaptans such as n-dodecylmercaptan, methylmercaptan or the like,mercaptan carboxylic acids such as mercaptoacetic acid,β-mercaptopropionic acid or the like, and cation exchange resins ororganic polymer siloxane containing a mercapto group, etc.

A solvent may or may not be used for the reaction, but if the molarratio of phenols/4-acylaralkylphenols is low or the phenols have a highmelting point and making it into solution is difficult, a solvent may beused. Examples of such solvent include lower aliphatic alcohols such asmethanol, butanol or the like, aromatic hydrocarbons such as toluene,xylene or the like, and aliphatic ketones such as methyl isobutyl ketoneor the like, and if the material used has a high melting point andeasily soluble in water such as catechol, water may be used as thereaction solvent. Lower aliphatic alcohol is preferred.

The amount of solvent used is not specifically limited, but it shouldnormally be in a range of 0.1 time by weight to 10 times by weight, orpreferably is in a range of 0.5 time by weight to 2 times by weight,relative to the phenols used.

The reaction temperature should normally be in a range of 0 to 100° C.,or preferably is in a range of 30 to 60° C.

The reaction is implemented by dripping a solvent solution of4-acylaralkylphenols into a solvent solution of phenols and catalyst inan ambience of nitrogen gas at 40° C., for example.

After the reaction, any known refining method can be used to refine thetarget product from the liquid reaction mixture, as necessary. Forexample, alkali water such as aqueous sodium hydroxide or the like isadded to the obtained liquid reaction mixture to neutralize the acid,and if necessary, solvent that can be separated from water such astoluene, xylene, methyl isobutyl ketone, ether or the like is added toseparate and remove the water layer, after which the water layer isseparated and removed to obtain the oil layer containing the targetproduct. The obtained oil layer is washed with water and, afterdistilling out the solvent, etc., from the obtained oil layer asnecessary, a solvent is added again to cause crystallization orprecipitation to obtain crystalline or non-crystalline solids. Ifnecessary, such as when the purity of crystal or solids is low, etc.,recrystallization or reprecipitation may be repeated once or multipletimes. By implementing processes A1, C1 and B1 in this sequence (firstproducing method), the target product of the producing method proposedby the present invention, or highly pure trisphenol, can be obtained.

Next, processes B2 and C2 in the producing method proposed by thepresent invention are explained.

Process B2 is a reaction process to obtain monoester-substitutedtrisphenol expressed by general formula (8) by causing4-acylaralkylphenylesters expressed by general formula (7) as obtainedby process A1 above to undergo condensation reaction with phenolsexpressed by general formula (4) according to the above reaction scheme,while process C2 is a reaction process to obtain the target product, ortrisphenols expressed by general formula (1), by subsequentlyhydrolyzing, alcoholyzing and/or phenolyzing the ester group of theobtained monoester-substituted trisphenol.

Here, the phenols expressed by general formula (4) is the same as thephenols mentioned in connection with process B1 above. Also in thecondensation reaction of 4-acylaralkylphenylesters and phenols, the acylgroup bonded to the 4-position of the phenyl group is reacted, whichmeans that, just like in the condensation reaction mentioned inconnection with process B1 above, similar conditions can be used for themolar ratio of phenols and material compound(4-acylaralkylphenylesters), catalyst and its amount, use ofco-catalyst, solvent and its amount, reaction temperature, reactionmethod, etc. In this reaction in process B2, the ester group of the4-acylaralkylphenylesters expressed by general formula (7) may bepartially hydrolyzed or shift to the hydroxyl group of the reactionproduct, etc., but it will not affect the reaction yield at all becausethe ester group is hydrolyzed next.

After the reaction, any known refining method can be used to refine thetarget product from the liquid reaction mixture, as necessary. Forexample, a method similar to the one mentioned in connection withprocess B1 above can be used to obtain monoester-substituted trisphenolsexpressed by general formula (8).

Next in process C2, the ester group of the monoester-substitutedtrisphenols obtained above is hydrolyzed, alcoholyzed and/or phenolyzed.

Any known method can be used for hydrolysis, alcoholysis and/orphenolysis of the ester group of the monoester-substituted trisphenols.In the case of decomposition using water, alcohol and/or phenol, forexample, conditions similar to those for hydrolysis, alcoholysis and/orphenolysis as mentioned in connection with process C1 above can be usedfor the molar ratio of water, alcohols and/or phenols and materialcompound (monoester-substituted trisphenols), alkali and its amount, useof solvent and its amount, reaction temperature, reaction method, etc.If an acid catalyst is used, it may be hydrochloric acid, hydrogenchloride gas, sulfuric acid, p-toluenesulfonic acid or methanesulfonicacid, etc., while the amount of acid catalyst used should normally be ina range of 0.1 to 10 mol, or preferably is in a range of 1 to 5 mol, permol of the ester group in the material compound. After the reaction, anyknown refining method can be used to refine the target product from theliquid reaction mixture, as necessary. For example, a method similar tothe one mentioned in connection with process C1 above can be used. Byimplementing processes A1, B2 and C2 in this sequence (second producingmethod), the target product of the present invention, or trisphenolsexpressed by general formula (1), can be obtained. When the4-acylaralkylphenylester expressed by general formula (7) as obtained byprocess A1 is reacted in the subsequent process, if reaction conditionsfor condensation reaction (process B1 or B2) and compounds used arecommon to reaction conditions and compounds used for hydrolysis,alcoholysis or phenolysis (process C1 or C2), the condensation reactionand hydrolysis, alcoholysis or phenolysis can be implemented in the sameprocess. Even if the conditions are such that either reaction isincomplete, the reaction product may be isolated and the incompletereaction can be continued, or the reaction product may be refined toobtain the target trisphenol.

Also when the material 4-aralkylphenol derivative expressed by generalformula (2) is 4-aralkylphenylethers expressed by general formula (2c)whose X is a hydrocarbon group, a method for producing trisphenols canbe presented that comprises either the producing method where processesA2, C3 and B1 mentioned above are implemented in this sequence (thirdproducing method), or producing method where processes A2, B3 and C4 areimplemented in this sequence (fourth producing method).

Process A2: Nucleus-acylate 4-aralkylphenylethers expressed by generalformula (2c)

(in the formula, R₁ to R₄, R₅ and R₆, R₀ and n are the same as thecorresponding items in general formula (2), while R represents ahydrocarbon group, where if n is 1 or greater, R₀ is not substituted atthe 4-position of the phenyl group) to obtain 4-acylaralkylphenylethersexpressed by general formula (9)

(in the formula, R₁ to R₄, R₅ and R₆, R₀ and n, and R₇ are the same asthe corresponding items in general formula (1), while R is the same as Rin general formula (2c)).

Process C3: Cleave the ether group of the 4-acylaralkylphenylethersexpressed by general formula (9) as obtained by process A2 to obtain4-acylaralkylphenol expressed by general formula (6) above.

Process B3: Cause the 4-acylaralkylphenylethers obtained by process A2to undergo condensation reaction with phenols expressed by generalformula (4) above, to obtain monoether substituted trisphenol expressedby general formula (10)

(in the formula, R₁ to R₄, R₅ and R₆, R₀ and n, R₇, and R₉ to R₁₁ arethe same as the corresponding items in general formula (1), while R isthe same as the corresponding item in general formula (2c)).

Process C4: Cleave the ether group of the monoether substitutedtrisphenol expressed by general formula (10) as obtained by process B3to obtain trisphenols expressed by general formula (1).

Here, the nucleus-acylation reaction in process A2 is such thatacylation is implemented using acylation agent such as acetylchloride,acetic anhydride or the like to introduce an acyl group to the4-position of the phenyl nucleus of the aralkyl group, in order toobtain 4-acylaralkylphenylethers expressed by general formula (9). Anyknown acylation reaction can be used. For example, it may be similar tothe nucleus-acylation reaction in the second stage of the two-stageacylation reaction method (process A1a) described in connection withprocess A1 above.

Also in process C3, any known cleavage reaction relating to phenylethercan be used. For example, implementing cleavage in the presence of BBr₃can selectively turn the alkoxyl group (RO group) into a hydroxy group.The subsequent condensation reaction of the obtained 4-acylaralkylphenolexpressed by general formula (6) and phenols expressed by generalformula (4) above is similar to that used in process B1 mentioned above.

Also in process B3, the condensation reaction of the4-acylaralkylphenylethers expressed by general formula (9) and phenolsexpressed by general formula (4) above may be similar to the methoddescribed in process B2 mentioned above.

Next in process C4, any known cleavage reaction relating to phenylethercan be used. For example, implementing cleavage in the presence of HBrcan turn the alkoxyl group (RO group) into a hydroxy group.

By sequentially implementing processes A2, C3 and B1 mentioned above(third producing method) or processes A2, B3 and C4 (fourth producingmethod) using 4-aralkylphenylethers expressed by general formula (2c) asthe starting material, the target product of the present invention, ortrisphenols expressed by general formula (1), can be obtained.

Also under the method for producing trisphenols expressed by generalformula (1) from 4-acylaralkylphenol derivative expressed by generalformula (3) where Xa is an organic sulfonyl group (R′—SO₂ group; R′represents a hydrocarbon group), any known elimination reaction(decomposition reaction) relating to sulfonyloxy group can be used if4-acylaralkylphenols expressed by general formula (6) are obtained byeliminating the Xa group in the 4-acylaralkylphenol derivative. If Xa isa tosyl group, for example, hydrolyzing it using alkali such aspotassium carbonate, potassium hydroxide or the like turns the tosyloxygroup into a hydroxyl group. If Xa is a mesyl group, cleavage reactionusing phenylmagnesiumbromide or phenyllithium turns the mesyloxy groupinto a hydroxyl group. Next, the obtained 4-acylaralkylphenols expressedby general formula (6) are passed through process B1 mentioned above toobtain the target trisphenols. Or in the case of condensation reactionof 4-acylaralkylphenol derivative expressed by general formula (3) withphenols expressed by general formula (4), conditions similar to thoseused in the condensation reaction mentioned in connection with processB1 or B2 above may be used for the molar ratio of phenols and materialcompound, catalyst and its amount, use of co-catalyst, solvent and itsamount, reaction temperature, reaction method, etc., and thereafter anyknown method mentioned above can be used to eliminate the sulfonyl groupin the obtained trisphenol derivative expressed by general formula (5)to obtain the target trisphenols.

Example 1 Synthesis of 4-(1-(4-acetoxyphenyl)-1-methylethyl)acetophenone(Process A1b)

Into a 500-ml four-way flask fitted with a drip funnel, cooling tube andagitator, 70.5 g (0.542 mol) of aluminum chloride and 105.8 g (1.5 timesby weight of aluminum chloride) of chloroform were introduced and thesystem was cooled to 5° C. while substituting the interior withnitrogen. After the cooling, 42.3 g (0.542 mol) of acetyl chloride wasdripped from the drip funnel over a period of 1 hour to form a complex.The complex did not dissolve in chloroform at 5° C. and slurry solutionwas created in the system.

After the complex had been formed, a solution prepared by dissolving50.0 g (0.236 mol) of p-cumylphenol in 75 g (1.5 times by weight ofp-cumylphenol) of chloroform was dripped into the complex solution overa period of 3 hours by maintaining the temperature in the flask at 5° C.and, after the entire volume had been dripped, the mixture was caused toreact at 20° C. for 2 hours.

When the reaction was complete, 171.8 g (0.5 time by weight of thecontent in the flask) of toluene was added to the liquid reactionmixture.

Next, 275.1 g of water was introduced into a 1-L four-way flask fittedwith a reflux cooling tube and agitator, and the aforementioned toluenesolution of liquid reaction mixture was dripped into this flask bymaintaining the temperature in the flask at 40 to 50° C.

After the entire volume had been dripped, 103.1 g of 35% hydrochloricacid was added and the mixture was agitated for 1 hour at 30° C., afterwhich the water layer was separated and removed. The obtained organiclayer was neutralized by adding an aqueous solution of sodium hydroxide,after which the water layer was removed and then chloroform wasdistilled out at normal pressure.

Next, water was added to the obtained solution to wash it, and the waterlayer was separated and removed, and then 100 g of 16% aqueous solutionof sodium hydroxide was added to the oil layer and the mixture wasagitated for 1 hour for the purpose of washing, after which 75%phosphoric acid was added to neutralize the mixture and remove the waterlayer. The obtained oil layer was distilled to 10 kPa at 60° C. toremove toluene. Then, 73.9 g of toluene and 73.9 g of isooctane wereadded to the residue after distillation, after which the mixture washeated and dissolved, crystallized, cooled, filtered and dried to obtain42.3 g of light yellowish white crystal with a purity of 97.3% based onhigh-performance liquid chromatography (hereinafter sometimes referredto as “HPLC”). When this crystal was analyzed by NMR and massspectrometry, it was confirmed as4-(1-(4-acetoxyphenyl)-1-methylethyl)acetophenone.

¹H-NMR (400 MHz, CDCl₃, standard substance: tetramethylsilane)

7.86 (aromatic H, 2H, double lines, J=8.78 Hz, b in the figure), 7.32(aromatic H, 2H, double lines, J=8.78 Hz, c in the figure), 7.200(aromatic H, 2H, double lines, J=8.78 Hz, e in the figure), 6.99(aromatic H, 2H, double lines, J=8.78 Hz, f in the figure), 2.57(CH₃CO—, 3H, single line, a in the figure), 2.28 (acetoxy, 3H, singleline, g in the figure), 1.69 (methyl, 6H, single line, d in the figure)

Example 2 Synthesis of 4-(1-(4-hydroxyphenyl)-1-methylethyl)acetophenone(Process C1)

From the crystal obtained in Example 1, 20.1 g was dissolved in 20 g oftoluene, to which 24.0 g of 16% aqueous solution of sodium hydroxide and2 g of methanol were added and the mixture was hydrolyzed for 2.5 hoursat 50° C. When the reaction was complete, the mixture was neutralized by75% phosphoric acid, after which the water layer was removed.

The obtained oil layer was distilled to 10 kPa at 60° C. to removetoluene, to obtain 18.0 g of orange solid with a purity of 99.9% basedon HPLC.

When this solid was analyzed by NMR and mass spectrometry, it wasconfirmed as 4-(1-(4-hydroxyphenyl)-1-methylethyl)acetophenone.

The yield relative to p-cumylphenol was 60.0%.

¹H-NMR (400 MHz, CDCl₃, standard substance: tetramethylsilane)

7.86 (aromatic H, 2H, double lines, J=8.78 Hz, b in the figure), 7.32(aromatic H, 2H, double lines, J=8.78 Hz, c in the figure), 7.07(aromatic H, 2H, double lines, J=8.78 Hz, e in the figure), 6.76(aromatic H, 2H, double lines, J=8.78 Hz, f in the figure), 5.95(hydroxyl, 1H, broad single line, g in the figure), 2.57 (CH₃CO—, 3H,single line, a in the figure), 1.67 (methyl, 6H, single line, d in thefigure)

Example 3 Synthesis of1-(α,α-bis(4-hydroxyphenyl)ethyl)-4-(α-methyl-α-(4-hydroxyphenyl)ethyl)benzene(Process B1)

Into a 300-ml four-way flask fitted with a drip funnel, cooling tube andagitator, 55.6 g of phenol and 1.7 g (3 percent by weight of phenolintroduced) of toluene were introduced, after which dodecylmercaptan(12.5 percent by mol of material ketone) was introduced, and the systemwas heated to 40° C. while substituting the interior with nitrogen.

After having been substituted with nitrogen, the interior of the systemwas substituted with hydrogen chloride gas. While supplying hydrogenchloride gas, a solution prepared by dissolving 24.6 g (0.096 mol) ofthe 4-[1-methyl-1-(4-hydroxyphenyl)ethyl]acetophenone obtained byExample 2 in 24.6 g of phenol was dripped into the flask over a periodof 3 hours while maintaining the temperature in the flask at 40 to 45°C.

After the entire volume had been dripped, the mixture was agitated for18 hours at 40° C. to continue with the reaction. When the reaction wascomplete, 35.7 g of toluene was added to the reaction mixture, afterwhich 16% aqueous solution of sodium hydroxide was added to neutralizethe mixture, which was then heated to 87° C. to dissolve the crystal.This was followed by crystallization and cooling to 30° C., after whichprecipitated crystal was filtered out and dried to obtain 58.7 g ofwhite crystal with a purity of 96.5% based on high-performance liquidchromatography (HPLC).

The obtained crystal was heated and dissolved in toluene, followed bycrystallization. The crystallized solution was cooled and crystal wasfiltered out and dried to obtain 99.6% white crystal. When this crystalwas analyzed by proton NMR and mass spectrometry, it was confirmed asthe target, or1-α-methyl-α,α-bis(4-hydroxyphenyl)ethyl)-4-(α-methyl-α-(4-hydroxyphenyl)ethyl)benzene.

Molecular weight: 423 (M-H)⁻ (liquid chromatography mass spectrometry)

¹H-NMR (400 MHz, CD₃OD, standard substance: tetramethylsilane) 7.01 to7.05 (4H, m), 6.92 (2H, d, J=7.81 Hz), 6.85 (4H, d, J=7.81 Hz), 6.62 to6.67 (6H, m), 4.85 (3H, brs), 2.01 (3H, s), 1.58 (6H, s)

Example 4 Synthesis of 4-(1-(4-hydroxyphenyl)-1-methylethyl)acetophenone(Process A1b+Process C1)

Into a 2-L four-way flask fitted with a drip funnel, cooling tube andagitator, 306.7 g (2.30 mol) of aluminum chloride and 460.0 g (1.5 timesby weight of aluminum chloride) of chloroform were introduced and thesystem was cooled to 5° C. while substituting the interior withnitrogen. After the cooling, 117.4 g (1.15 mol) of acetic anhydride wasdripped from the drip funnel over a period of 1 hour under agitation toform a complex. The complex did not dissolve in chloroform at 5° C. andtherefore slurry solution was created.

Thereafter, a solution prepared by dissolving 106.0 g (0.50 mol) ofp-cumylphenol in 159.1 g (1.5 times by weight of p-cumylphenol) ofchloroform was dripped into the slurry solution over a period of 3 hoursat 5° C. under agitation and, after the entire volume had been dripped,the mixture was caused to react at 5° C. for another 2 hours underagitation.

When the reaction was complete, 619.0 g of toluene was added to dilutethe liquid reaction mixture. Next, 574.6 g of water was introduced intoa 3-L four-way flask fitted with a cooling tube and agitator, and theaforementioned toluene-diluted reaction liquid was dripped into thiswater at 10 to 20° C. under agitation. After the entire volume had beendripped, 346.5 g of 35% hydrochloric acid was added and the mixture wasagitated for 1 hour at 50° C. Thereafter, precipitated solids werefiltered out and the water layer constituting the filtrate was separatedand removed. After neutralizing the obtained oil layer by adding 16%aqueous solution of sodium hydroxide, 35% hydrochloric acid was addedand the mixture was agitated for the purpose of washing, after which thewater layer was separated and 16% aqueous solution of sodium hydroxidewas added again to the obtained oil layer to neutralize the mixture. Thewater layer was separated and removed and the obtained oil layer wasdistilled to remove 419.5 g of solvent, and water was added to theobtained residual liquid after distillation and the mixture wasagitated, and then the water layer was separated and removed. Next,127.6 g of 16% aqueous solution of sodium hydroxide and 36.1 g ofmethanol were added to the obtained oil layer and the mixture washydrolyzed for 2 hours at 50° C. under agitation. When the reaction wascomplete, 75% phosphoric acid was added to neutralize the mixture, andthen the water layer was separated and removed and water was added towash the oil layer, after which the water layer was separated andremoved and the obtained oil layer was distilled at 70° C. underdecompression to remove toluene. Then to the residula liquid afterdistillation, 56.1 g (0.5 time by weight of the residula liquid afterdistillation) of methylisobutylketone and 224.5 g (2 times by weight ofresidual liquid after distillation) of cyclohexane were added and themixture was heated and dissolved, followed by crystallization, filteringand drying to obtain 65.7 g of white powder. When this crystal wasanalyzed by proton NMR and mass spectrometry, it was confirmed as4-(1-(4-hydroxyphenyl)-1-methylethyl)acetophenone.

The yield relative to p-cumylphenol was 50.3%.

Example 5 Synthesis of 1-acetoxy-4-(1-methyl-1-phenylethyl)benzene(Process A1a, First Stage)

Into a 500-ml four-way flask fitted with a drip funnel, cooling tube andagitator, 100 g (0.471 mol) of p-cumylphenol, 50.0 g (0.832 mol) ofglacial acetic acid and 0.6 g (0.832 mol) of 75% phosphoric acid wereintroduced and the system was heated to a range of 90 to 95° C. whilesubstituting the interior with nitrogen. After the heating, 57.7 g(0.565 mol) of acetic anhydride was dripped over a period of 1 hourwhile maintaining the internal temperature at 90 to 95° C. to causereaction. After the dripping, the mixture was agitated for 3 hours atthe same temperature to cause reaction. When the reaction was complete,acetic acid was removed by distillation under decompression, and 200 gof cyclohexane was added to dissolve the residue after distillation.Next, 10% aqueous solution of sodium carbonate was added to thissolution and the mixture was agitated, after which the water layer wasseparated and removed. Then, 10% aqueous solution of sodium carbonatewas added to the obtained organic layer, followed by washing and removalof the water layer using similar operations.

Distilled water was added further to the obtained organic layer and themixture was agitated, after which the water layer was separated andremoved. Similarly, water was added to the obtained oil layer for thepurpose of water washing, followed by removal of the water layer, andthis operation was performed twice. Cyclohexane was distilled out fromthe obtained organic layer, to obtain colorless, clear liquid with apurity of 98.2% based on gas chromatography.

When this liquid was analyzed by NMR and mass spectrometry, it wasconfirmed as 1-acetoxy-4-(1-methyl-1-phenylethyl)benzene.

The yield relative to p-cumylphenol was 98.4%.

Molecular weight: 254 (gas chromatography mass spectrometry)

1H-NMR (400 MHz, CDCl₃, standard substance: tetramethylsilane)

1.67 (6H, s), 2.27 (3H, s), 6.96 to 6.98 (2H, m), 7.17 to 7.26 (7H, m)

Example 6 Synthesis of 4-[1-(4-acetoxyphenyl)-1-methylethyl]acetophenone(Process A1a, second stage)

Into a 1-L four-way flask fitted with a drip funnel, cooling tube andagitator, 98.1 g (0.736 mol) of aluminum chloride and 147.2 g ofdichloromethane were introduced and the system was cooled to 5° C. whilesubstituting the interior with nitrogen. After the cooling, 37.6 g(0.368 mol) of acetic anhydride was dripped over a period of 1.5 hourswhile maintaining the temperature at 5 to 10° C. to form a complex.

After the complex had formed, a solution prepared by dissolving 76.3 g(0.30 mol) of the 1-acetoxy-4-(1-methyl-1-phenylethyl)benzene obtainedby Example 5 in 114.5 g of dichloromethane was dripped into the complexsolution over a period of 3 hours while maintaining the internaltemperature at 5 to 10° C. and, after the entire volume had beendripped, the mixture was caused to react at 5° C. for 1.5 hours. Whenthe reaction was complete, 400 g of toluene was added to the liquidreaction mixture.

Next, 250.0 g of distilled water was introduced into a 2-L four-wayflask fitted with a reflux cooling tube and agitator, and theaforementioned toluene solution of liquid reaction mixture was drippedinto this flask.

After the entire volume had been dripped, 93.4 g of 25% hydrochloricacid was added to the organic layer obtained by separating and removingthe water layer, and the mixture was agitated for 30 minutes at 30° C.,after which the water layer was separated and removed. Next, 93.4 g of25% hydrochloric acid was added to the obtained organic layer, followedby washing and removal of the water layer using similar operations.Aqueous solution of sodium hydroxide was added to the obtained organiclayer to neutralize the layer, after which the water layer was separatedand removed and then distilled water was added to the organic layer, andthe mixture was agitated, after which the water layer was separated andremoved. Distilled water was added to the organic layer, followed bywashing and removal of the water layer using similar operations.

Thereafter, solvent was distilled out from the obtained organic layerunder decompression.

Next, 45.5 g of methylisobutylketone and 135.6 g of cyclohexane wereadded to the residue after distillation, followed by cooling andcrystallization. Precipitated crystal was filtered out and dried toobtain 19.5 g of white crystal, or4-[1-(4-acetoxyphenyl)-1-methylethyl]acetophenone, with a purity of97.6% based on gas chromatography.

Example 7 Synthesis of1-[α,α-bis(4-hydroxyphenyl)ethyl]-4-[α-methyl-α-(4-hydroxyphenyl)ethyl]benzene

Into a 200-ml four-way flask fitted with a drip funnel, cooling tube andagitator, 22.6 g (0.240 mol) of phenol, 0.7 g (3 percent by weight ofphenol introduced) of toluene and 0.5 ml of dodecyl mercaptan wereintroduced and the system was heated to 45° C. while substituting theinterior with nitrogen.

After having been substituted with nitrogen, the interior of the systemwas substituted with hydrogen chloride gas. A solution prepared bydissolving 11.2 g (0.038 mol) of the4-[1-(4-acetoxyphenyl)-1-methylethyl]acetophenone obtained by Example 6in 11.2 g (0.119 mol) of phenol was dripped into the flask over a periodof 1.5 hours while maintaining the temperature in the flask at 45° C.Supply of hydrochloric acid gas into the system was continued whiledripping. When the entire volume had been dripped, the mixture wasagitated for 21 hours at 50° C. to continue with the reaction. When thereaction was complete, 50.0 g of toluene and 10.0 g of distilled waterwere added to the reaction mixture, after which 16% aqueous solution ofsodium hydroxide was added to neutralize the mixture, which was thenheated to 85° C. to dissolve the crystal and the water layer wasseparated and removed. Distilled water was added to the obtained organiclayer for the purpose of washing with water, followed by separation andremoval of the water layer, and this operation was performed twice. Theobtained organic layer was crystallized and precipitated crystal wasfiltered out and dried to obtain 13.6 g of white crystal, or1-[α,α-bis(4-hydroxyphenyl)ethyl]-4-[a-methyl-a-(4-hydroxyphenyl)ethyl]benzene,with a purity of 95.5% based on high-performance liquid chromatography.

The yield relative to 4-(1-(4-acetoxyphenyl)-1-methylethyl)acetophenonewas 83.2%.

1. A method for producing trisphenols expressed by general formula (1)

(wherein R₁ to R₄ each independently represent a hydrogen atom, alkylgroup, alkoxyl group, aromatic hydrocarbon group, halogen atom, acyloxygroup or hydroxyl group; R₅ and R₆ each independently represent ahydrogen atom or alkyl group; R₇ represents a hydrogen atom or alkylgroup; R₀ represents an alkyl group, alkoxyl group or halogen atom; n is0 or an integer of 1 to 4, where if n is 2 or greater, all R₀'s may bethe same or different; and R₉ to R₁₁ each independently represent ahydrogen atom, alkyl group, alkoxyl group, aromatic hydrocarbon group,halogen atom or hydroxyl group), said producing method characterized byusing as a starting material 4-aralkylphenol derivatives expressed bygeneral formula (2)

(wherein R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (1), while X represents ahydrogen atom or leaving group that can be substituted with a hydrogenatom, where if n is 1 or greater, R₀ is not substituted at the4-position of the phenyl group).
 2. A method for producing trisphenolsaccording to claim 1, wherein the leaving group that can be substitutedwith a hydrogen atom, expressed by X in general formula (2), is an acylgroup.
 3. A method for producing trisphenols according to claim 1,characterized by comprising a nucleus-acylation process (A) as well assubsequent phenols condensation process (B) and elimination process (C)for substituting Xa with a hydrogen atom: Process (A): Nucleus-acylate4-aralkylphenol derivatives expressed by general formula (2) above toobtain 4-acylaralkylphenol derivatives expressed by general formula (3)

(wherein R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (2), while R₇ is the same as thecorresponding item in general formula (1) and Xa represents a leavinggroup that can be substituted with a hydrogen atom); Process (B): Causephenols expressed by general formula (4)

(wherein R₉ to R₁₁ are the same as the corresponding items in generalformula (1)) to undergo condensation reaction with the4-acylaralkylphenol derivatives expressed by general formula (3) aboveas obtained by process (A), to obtain trisphenol derivatives expressedby general formula (5)

(wherein R₁ to R₄, R₅ and R₆, R₀ and n, R₇, and R₉ to R₁₁ are the sameas the corresponding items in general formula (1), while Xa represents aleaving group that can be substituted with a hydrogen atom) or, causethe phenols above to undergo condensation reaction with the4-acylaralkylphenols expressed by general formula (6) as obtained byprocess (C), to obtain trisphenols expressed by general formula (1); andProcess (C): Eliminate the Xa group of the 4-acylaralkylphenolderivatives expressed by general formula (3) as obtained by process (A),to obtain 4-acylaralkylphenols expressed by general formula (6)

(wherein R₁ to R₄, R₅ and R₆, R₀ and n, and R₇ are the same as thecorresponding items in general formula (1)) or, eliminate the Xa groupof the trisphenol derivatives expressed by general formula (5) asobtained by process (B), to obtain trisphenols expressed by generalformula (1).
 4. A method for producing trisphenols according to claim 1,wherein when general formula (2) above is expressed as general formula(2a) where X is an acyl group, or as general formula (2b) where X is ahydrogen atom, said producing method comprising processes A1, C1 and B1in this sequence (first producing method) or processes A1, B2 and C2 inthis sequence (second producing method): Process A1: Nucleus-acylate4-aralkylphenylesters expressed by general formula (2a)

(wherein R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (2), while R₈ represents ahydrogen atom or hydrocarbon group, where if n is 1 or greater, R₀ isnot substituted at the 4-position of the phenyl group) or,4-aralkylphenols expressed by general formula (2b)

(wherein R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (2), where if n is 1 or greater,R₀ is not substituted at the 4-position of the phenyl group) to obtain4-acylaralkylphenylesters expressed by general formula (7)

(wherein R₁ to R₄, R₅ and R₆, R₀ and n, and R₇ are the same as thecorresponding items in general formula (1), while R₈ is the same as thecorresponding item in general formula (2a)); Process C1: Hydrolyze,alcoholyze or phenolyze the ester group of the 4-acylaralkylphenylestersexpressed by general formula (7), to obtain 4-acylaralkylphenolsexpressed by general formula (6)

(wherein R₁ to R₄, R₅ and R₆, R₀ and n, and R₇ are the same as thecorresponding items in general formula (1)); Process B1: Next, cause theobtained 4-acylaralkylphenols to undergo condensation reaction withphenols expressed by general formula (4)

(wherein R₉ to R₁₁ are the same as the corresponding items in generalformula (1)) to obtain trisphenols expressed by general formula (1);Process B2: Cause 4-acylaralkylphenylesters expressed by general formula(7) to undergo condensation reaction with phenols expressed by generalformula (4), to obtain monoester-substituted trisphenols expressed bygeneral formula (8)

(wherein R₁ to R₄, R₅ and R₆, R₀ and n, R₇, and R₉ to R₁₁ are the sameas the corresponding items in general formula (1), while R₈ is the sameas the corresponding item in general formula (2a)); and Process C2:Next, hydrolyze, alcoholyze or phenolyze the ester group of the obtainedmonoester-substituted trisphenols, to obtain trisphenols expressed bygeneral formula (1).
 5. A method for producing trisphenols according toclaim 4, wherein the condensation reaction with phenols is implementedalong with the hydrolysis reaction, alcoholysis reaction and/orphenolysis reaction in a same process.
 6. A method for producingtrisphenol derivatives expressed by general formula (5)

(wherein R₁ to R₄ each independently represent a hydrogen atom, alkylgroup, alkoxyl group, aromatic hydrocarbon group, halogen atom, acyloxygroup or hydroxyl group, R₅ and R₆ each independently represent ahydrogen atom or alkyl group, R₇ represents a hydrogen atom or alkylgroup; R₀ represents an alkyl group, alkoxyl group or halogen atom; n is0 or an integer of 1 to 4, where if n is 2 or greater, all R₀'s may bethe same or different and R₉ to R₁₁ each independently represent ahydrogen atom, alkyl group, alkoxyl group, aromatic hydrocarbon group,halogen atom or hydroxyl group), said method comprising: Process (A):Nucleus-ac late 4-aralkylphenol derivatives expressed by general formula(2) to obtain 4-acylaralkylphenol derivatives expressed by generalformula (3)

(wherein R₁ to R₄ R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (5), while X represents ahydrogen atom or leaving group that can be substituted with a hydrogenatom, where if n is 1 or greater, R₀ is not substituted at the4-position of the phenyl group);

(wherein R₁ to R₄, R₅ and R₆, and R₀ and n are the same as thecorresponding items in general formula (2), while R₇ and Xa are the sameas the corresponding items in general formula (5)); and Process (B):Cause phenols expressed by general formula (4)

(wherein R₉ to R₁₁ are the same as the corresponding items in generalformula (5)) to undergo condensation reaction with the4-acylaralkylphenol derivatives expressed by general formula (3) aboveas obtained by process (A), to obtain the trisphenol derivativesexpressed by general formula (5).
 7. 4-Acylaralkylphenols expressed bygeneral formula (6)

wherein R₁ to R₄ each independently represent a hydrogen atom, alkylgroup, alkoxyl group, aromatic hydrocarbon group, halogen atom, acyloxygroup or hydroxyl group; R₅ and R₆ each independently represent ahydrogen atom or alkyl group; R₇ represents a hydrogen atom or alkylgroup; R₀ represents an alkyl group, alkoxyl group or halogen atom; andn is 0 or an integer of 1 to 4, where if n is 2 or greater, all R₀'s maybe the same or different.
 8. 4-Acylaralkylphenol derivative expressed bygeneral formula (7)

wherein R₁ to R₄ each independently represent a hydrogen atom, alkylgroup, alkoxyl group, aromatic hydrocarbon group, halogen atom, acyloxygroup or hydroxyl group; R₅ and R₆ each independently represent ahydrogen atom or alkyl group; R₇ represents a hydrogen atom or alkylgroup; R₈ represents a hydrogen atom or hydrocarbon group; R₀ representsan alkyl group, alkoxyl group or halogen atom; and n is 0 or an integerof 1 to 4, where if n is 2 or greater, all R₀'s may be the same ordifferent.